THE EFFECT OF FLUORIDE PRETREATMENT ON SHEAR BOND STRENGTH BETWEEN ENAMEL AND FISSURE SEALANT
 
불소 전처리가 법랑질과 치면열구전색재의 전단결합강도에 미치는 영향
유필준, 장기택, 김종철
서울대학교 치과대학 소아치과학교실 및 치학연구소
Abstract
This study seeks to know the effect of fluoride topical application on the shear bond strength between enamel and fissure sealant. On group 1,2,3,4, Teethmate A(unfilled sealant) and on group 5,6,7,8 Ultraseal XT(filled sealant) were used. Group 1 and 5 were not pre-treated with fluoride and group 2 and 6 were pre-treated with 1.23% APF for 4minutes. Group 3 and 7 were pretreated with 2.0% NaF for 4 minutes. and group 4 and 8 were pumiced with abrasive containing fluoride for 10 seconds. Prepared specimens were acid etched for 30 seconds using 35% phosphoric acid, and then sealant was cured to the specimen using a 3mm diameter by 2mm height mold. They went through thermocycling. Its shear bond strength was measured, and then acid etched both groups that were pretreated with fluoride and that were not pretreated with fluoride. Then we examined the surface of the specimen with EM and came up with these results. In groups using unfilled sealant(group 1,2,3.4) there were no significant differences between oops pretreated with fluoride and groups not pretreated with fluoride. In groups using filled sealant(group 5,6,7,8), groups 6 and 7(treated with 1.23% APF 2.0% NaF respectively) showed significantly lower shear bond strength, compared to group 5 (not pretreated with fluoride) and group 8 (pumiced with abrasive containing fluoride) (p<0.05).
Key Words: Fluoride, Fissure sealant, Shear bond strength


ABOUT
BROWSE ARTICLES
EDITORIAL POLICY
FOR CONTRIBUTORS
Editorial Office
Seoul National University, Dental Hospital, B1-166 101, Daehak-ro, Jongno-gu, Seoul 03080, Republic of Korea
Tel: +82-70-4145-8875    Fax: +82-2-745-8875    E-mail: info@kapd.org                

Copyright © 2024 by Korean Academy of Pediatric Dentistry.

Developed in M2PI

Close layer
prev next