An Experimental Study on the Fracture and Shear Bonding Strength of Resin-modified Glass lonomer Cements
 
Resin-modified glass ionomer cements의 파절 및 저단결합강도에 관한 실험적 연구
김재곤, 양철희, 안수현, 노용관, 백병주
전북대학교 치과대학 소아치과학교실 및 치의학연구소
Abstract
The purpose of this study was to compare the fracture and shear bonding strength of resin-modified glass ionomer cements with composite resin and conventional glass ionomer cement Three kinds of restorative materials including a composite resin (Z 100), a conventional glass ionomer cement(Fuji II), and resin- modified glass ionomer cements(Fuji II LC, Vitremer, Dyract and Compoglass) were investigated in this study. For measurement of fracture and shear bonding strength, disk samples of the materials were prepared and cylindrical samples of the materials were bonded the flat enamel and dentin surfaces according to manufactuer's instructions. All specimen were determinated by using an Instron testing machine with a crosshead speed of 1 mm/min. Then, each treated enamel and dentin surface was observed by SEM. The following results were obtained. 1. The bi-axial flexural strength of Z 100 was highest, and Fuji n LC, Vitremer, Dyract and Compoglass were significantly higher than Fuji n (P<0.05). 2. The shear bonding strength of Z 100 on the enamel and dentin surface was higher than other experimental groups except Fuji II LC(P<0.05). Fuji II LC was significantly higher than Fuji II (P<0.05), but in the case of Vitremer, Dyract and Compoglass were similar to Fuji II (P>0.05). 3. The shear bonding strength of Z 100 and Fuji II LC on the enamel surface were highly increased as compared with dentin surface (P<0.05), but in the case of Fuji II, Vitremer, Dyract and Compoglass were not different between enamel and dentin(P>0.05). 4. In the Z 100 and Fuji II LC, obvious etched enamel surface and exposed dentinal tubules according to remove of smear layer and smear plug were observed.


ABOUT
BROWSE ARTICLES
EDITORIAL POLICY
FOR CONTRIBUTORS
Editorial Office
Seoul National University, Dental Hospital, B1-166 101, Daehak-ro, Jongno-gu, Seoul 03080, Republic of Korea
Tel: +82-70-4145-8875    Fax: +82-2-745-8875    E-mail: info@kapd.org                

Copyright © 2024 by Korean Academy of Pediatric Dentistry.

Developed in M2PI

Close layer
prev next