| A STUDY ON THE MODE OF POLYMERIZATION OF LIGHT-CURED RESTORATIVE MATERIALS CURED WITH THREE DIFFERENT LIGHT SOURCES |
| |
| 광원의 유형에 따른 광중합 수복재의 중합양상 |
|
권민석, 정태성, 김신 |
|
부산대학교 치과대학 소아치과학교실 |
|
|
|
|
| Abstract |
|
The purpose of this study was to compare the effect of exposure time on the polymerization of surface and 2 mm below the surface of light-cured restorative materials cured with three different light sources; conventional halogen light curing unit(XL 3000, 3M, U.S.A.), plasma arc light curing unit(Flipo, LOKKI, France) and light emitting diode(LED) light curing unit(Elipar Free light, 3M, U.S.A.) and compare the uniformity of polymerization from the center to the periphery of resin surfaces according to polymerization diameter cure with three different light sources. From the experiment, the following results were obtained. 1. In Z-100, Plasma arc light exposure time of 6 to 9 seconds and LED light exposure time of 40 to 60 seconds produced microhardness values similar to those produced with 40 second exposure to a conventional halogen light(p>0.05). 2. In Tetric Flow, Plasma arc light exposure time of 9 seconds and LED light exposure time of 40 to 60 seconds produced microhardness values similar to those produced with 40 second exposure to a conventional halogen light(p>0.05). 3. In Dyract AP, Plasma arc light exposure time of 6 to 9 seconds and LED light exposure time of 20 to 40 seconds produced microhardness values similar to those produced with 40second exposure to a conventional halogen light(p>0.05). 4. In Fuji II LC, Plasma arc light exposure time of 9 seconds and LED light exposure time of 20 to 60 seconds produced microhardness values similar to those produced with 40second exposure to a conventional halogen light(p>0.05). 5. Except Fuji II LC, microhardness was decreased from the center to the periphery in all light sources(p<0.05). |
| Key Words:
Halogen, Plasma arc, Light emitting diode, Exposure time, Polymerization diameter |
|
PDF Links
Download Citation