An Experimental Study on the Shear Bond Strength of Fluoride-Containing Sealant and Non-Fluoride Containing Sealant
 
불소함유여부에 따른 치면열구전색제의 전단결합강도에 관한 실험적 연구
허선, 권선자, 김재곤, 백병주
전북대학교 치과대학 소아치과학교실
Abstract
This study was to evaluate shear bond strength of fluoride-releasing sealant and nonfluoride releasing sealant to enamel surface of bovine tooth. 80 extracted bovine teeth were randomly assigned to four groups, and four kinds of sealants including Teethmate-A(Kuraray Co.), Teethmate-F(Kuraray Co.), Helioseal(Vivadent Co.), Helioseal-F(Vivadent Co.) were bonded to exposed enamel surfaces using silicon plate. Shear bond strength was determined in an instron universal testing machine at a crosshead speed of 1mm/min. Then, the fracture surfaces of test specimens were investigated with scanning electron microscope. The obtained results were as follows; 1. The shear bond strength decreased in the following order : Teethmate-A(18.31MPa), Teethmate-F(11.90MPa), Helioseal (11.74 MPa), Helioseal-F(10.64MPa). 2. The shear bond strength of Teethmate-A showed significantly higher than that of Teethmate-F(P<0.05), but Helioseal and Helioseal-F didn't showed statistically different(P<0.05). 3. According to the SEM, Teethmate-A group showed cohesive failure, and Teethmate-A group & Helioseal group showed mixed pattern of cohesive and adhesive failure and Helioseal-F group showed adhesive failure.


ABOUT
BROWSE ARTICLES
EDITORIAL POLICY
FOR CONTRIBUTORS
Editorial Office
Seoul National University, Dental Hospital, B1-166 101, Daehak-ro, Jongno-gu, Seoul 03080, Republic of Korea
Tel: +82-70-4145-8875    Fax: +82-2-745-8875    E-mail: info@kapd.org                

Copyright © 2024 by Korean Academy of Pediatric Dentistry.

Developed in M2PI

Close layer
prev next