| MICROLEAKAGE TEST ACCORDING TO ACID ETCHING TREATMENT IN CLASS V COMPOMERS |
| |
| 치면 산처리가 V급 와동의 compomer 수복에서 미세누출에 미치는 영향 |
|
문상희, 이창섭, 이상호 |
|
조선대학교 치과대학 소아치과학교실 |
|
|
|
|
| Abstract |
|
The purpose of this study was to evaluate the microleakage of class V compomers according to acid etching treatment and treatment times. Extracted 180 sound human molar teeth were selected then prepared physiologic pulpal pressure far this experiment. In this study class V cavities were prepared on buccal surface with gingival margin located in 1mm superior to CEJ under simulate physiological conditions. These specimens were randomly divided into 6 groups of 30 each and restored following methods : A: Dyract AP + Prime&Bond 2.1 Group 1 : No acid etching, according to manufacturer's instruction. Group 2 : 15 seconds acid etching and same method with Group 1. Group 3 : 30 seconds acid etching and same method with Group 1. B: F2000 groups + Single Bond adhesive Group 1 : No acid etching, according to manufacturer's instruction. Group 2 : 15 seconds acid etching and same method with Group 1 Group 3 : 30 seconds acid etching and same method with Group 1. After 500 thermocycling between 5℃ and 55℃, the specimens were sealed with glass ionomer and nail varnish then placed in 5% methylene blue dye for 5 hours and rinsed with tab water. The specimens were embedded in orthodontic clear resin, then sectioned buccolingually through the center of restoration with a low speed diamond saw. The dye penetration on each of the specimens were then observed with a stereomicroscope at ×20 magnification. The results of this study were statistically analyzed using the indepedent sample t-test and analysis of variance. Results were as follows, 1. In occlusal walls, microleakage were significantly reduced in acid etched group restored with Dyract AP but no statistically significance in F2000 groups. 2. In gingival walls, microleakage were significantly reduced in group 2 restored with Dyract AP, and group 2 and group 3 in F2000 groups. 3. All groups, except group 3 in Dyract AP, showed significantly less microleakage in occlusal wall than gingival wall. 4. No statistical significance were showed between group 2 and group 3 in both materials. |
| Key Words:
Compomer, Microleakage, Acid etching, Physiologic pulpal pressure, Class V cavity |
|
PDF Links
Download Citation