Abstract

The purpose of this study was to measure and analyze the bond strength of bonded amalgam using dental adhesives and to compare this with light-curing composite resin. Sections 8mm in diameter were punched out from the labial surface of bovine anterior teeth. These were embedded in clear acrylic resin blocks with labial surface facing out. 55 specimens were made for enamel and dentin each. After dividing these into 5 groups, group 1: Superbond C&B, group 2: Panavia 21, group 3: All-Bond 2, group 4: Fuji I Glass Ionomer Luting Cement, group 5: Scotchbond Multi-Purpose(Restorative Z-100), molds with holes of 6.3mm in diameter and 1.5mm in depth were placed over the specimens. The exposed tooth surfaces were treated with adhesives and the molds were filled with amalgam. In group 5, the mold was filled with composite resin and light-cured for 40 seconds. The author measured all specimens for bond strength 24 hours after amalgam filing and analyzed fracture surfaces. The following results were obtained: 1. Among the dentin groups, groups 1, 2 and 4 showed significantly lower bond strength compared with group 5(P<0.05). 2. Among the enamel groups, group 4 showed significantly lower bond strength compared with group 5(P<0.05). 3. In group 2, 2D showed significantly lower bond strength compared with group 2E(P<0.05). Other adhesives showed no such differences in bond strength between dentin and enamel(P>0.05). 4. Cohesive failure was observed in groups 1E and 5D, while mixed failure was seen in groups 1 and 5. Only adhesive failures were noted in groups 2, 3, 4.

Key Words: Bond strength, bonded amalgam, failure mode