| USE OF ACRYLIC RESIN IN RELEASING CHLORHEXIDINE |
| |
| 아크릴릭 레진상을 이용한 클로르헥시딘의 방출에 관한 연구 |
|
이은영, 최영철 |
|
경희대학교 치과대학 소아치과학교실 |
|
|
|
|
| Abstract |
|
The purpose of this study was to develop a new way of delivery system of chlorhexidine using self-curing acrylic resin. Different preparations of chlorhexidine, such as chlorhexidine varnish(Chlorzoin®) and chlorhexidine diacetate crystalline, were mixed into self-curing acrylic resin with different methods. Every resin plate was made and was immersed in 100ml of distilled water individually, and kept in an incubator at 37℃. Solution(0.8ml) was collected from the each container at every 24 hours, and the amount of released chlorhexidine in the solution was measured in an ultraviolet spectrophotometer at 255nm. Flexural strength of all of the resin plates in the Experiment 2-A and 2-B were measured using Instron at the end of the experimental periods. The results were as follows: 1. It was found that chlorhexidine was released from the experimental groups in the Experiment 1, 2-A, and 2-B. And the release of chlorhexidine from all of the experimental groups showed a pattern of sustained-release preparation. 2. It seemed likely that a condition of "dryness" reduced a release of chlorhexidine from the chlorhexidine varnish. 3. It may be stated that a method of "chlorhexidine diacetate mix" with the polymer be more efficient than a method of "Chlorzoin mix" with the monomer. 4. Although it was evident that a flexural strength of the acrylic resin plates be reduced by a mix of either Chlorzoin or chlorhexidine diacetate crystalline, it seemed likely that the resin plates except Group 4 and 5 in the Experiment 2-B may be usable in the clinical situation. |
| Key Words:
Acrylic Resin, Chlorhexidine, Sustained-release, Flexural Strength |
|
PDF Links
Download Citation