Journal of the Korean Academy of Pediatric Dentistry 1997;24(2):428-435.
Published online May 31, 1997.
A STUDY ON THE FLUORIDE RELEASING AND FLEXURAL STRENGTH OF ACRYLIC RESIN BLENDED WITH FLUORIDE
 
불소를 포함시킨 가철성 교정장치용 Resin의 불소 방출과 굴곡강도에 관한 연구
장기택, 이상훈, 김종철, 한세현, 손동수
서울대학교 치과대학 소아치과학교실
Abstract
For the purpose of investigating the continuous fluoride releasing from acrylic resin using removable appliances by incorporating fluoride into polymethylmethacrylate during the construction of the appliances, two kinds of fluoride were blended with acrylic powder and devided into five groups as follows. Group 1 : no fluoride (control) Group 2 : NaF 5 wt% Group 3 : NaF 10 wt% Group 4 : CaF2 5 wt% Group 5 : CaF2 10 wt% Resin specimens were tested in vitro for fluoride release with fluoride electrode and flexural strength with Instron. The results were as follows ; 1. After 24 hrs, released fluoride concentration(ppm) was the most in group 3(126.5±14.15) then, next, group 2(49.5±4.92), group 5(2.67±1.08), group 4(0.81±0.30), group 1(0.03±0.01) in order, but after 28 days, group 3(3.37±0.31), group 5(1.25±0.25), group 4(0.74±0.19), group 2(0.68±0.07), group 1(0.03±0.01). 2. Fluoride releasing of NaF groups were faster and more amount than CaF2 groups initially but decreased significantly, later. 3. Flexural strength (kg/cm2) was the biggest in group 1(602.90±69.32), and then group 4(568.98±20.16), group 5(556.19±5.26), group 2(536.12±30.35), group 3(508.44±26.16) in order, the differences between control group and NaF groups were statistically significant (p<0.05).


ABOUT
BROWSE ARTICLES
EDITORIAL POLICY
FOR CONTRIBUTORS
Editorial Office
Seoul National University, Dental Hospital, B1-166 101, Daehak-ro, Jongno-gu, Seoul 03080, Republic of Korea
Tel: +82-70-4145-8875    Fax: +82-2-745-8875    E-mail: info@kapd.org                

Copyright © 2024 by Korean Academy of Pediatric Dentistry.

Developed in M2PI

Close layer
prev next