The effect of various surface coatings on microleakage and microhardness of light-cured glass ionomer restoration
 
수종 표면 보호재의 도포가 광중합형 유리 아이오너머 수복물의 변연 누출 및 미세 경도에 미치는 영향
김기섭, 김용기
단국대학교 치과대학 소아치과학교실
Abstract
The purpose of this study was to evaluate the efficacy of several surface coating agents in preventing microleakage and increasing microhardness of light-cured glass ionomer restoration. 50 and 25 sound molar teeth were used for the microleakage test and microhardness test respectively. Data were analyzed statistically using Kruskal-Wallis and/or Mann-Whitney test. The results of the present study were as follows: 1. The effect of surface coating in reducing microleakage was proven only at the gingival margin of restorations with statistical significance(p<.05). 2. The distribution of microleakage score at gingival margin was shown to be better than that of occlusal margin in general but with no statistically significant differences(p>.05). 3. No statistically significant differences in microhardness could be found between groups (p>.05) regardless of depth of measurement. 4. Under the present experimental conditions, the types or application of surface coating agents did not impose any significant effect on microhardness of glass ionomer restorative material whereas the protective effect of surface coating in reducing microleakage was partly proven.


ABOUT
BROWSE ARTICLES
EDITORIAL POLICY
FOR CONTRIBUTORS
Editorial Office
Seoul National University, Dental Hospital, B1-166 101, Daehak-ro, Jongno-gu, Seoul 03080, Republic of Korea
Tel: +82-70-4145-8875    Fax: +82-2-745-8875    E-mail: info@kapd.org                

Copyright © 2024 by Korean Academy of Pediatric Dentistry.

Developed in M2PI

Close layer
prev next