AN EXPERIMENTAL STUDY FOR MICROLEAKAGE OF AMALGAM USING RESIN ADHESIVE LINERS IN PRIMARY MOLAR TOOTH |
|
유구치 아말감 수복물에서 레진 접착성 이장재의 미세 변연 누출에 관한 비교 연구 |
김종태, 최병재, 이제호, 이종갑 |
연세대학교 치과대학 소아치과학교실 |
|
|
Abstract |
The purpose of this study was to compare the marginal leakage of resin liner which was used as a liner to amalgam restoration. Control group composed of no liner group, copalite group and experimental group composed of All-bond 2, Vitrebond, Superbond D-liner applied groups were evaluated. Cl.V preparation with a size of 3×2×1.5mm on 70 extracted primary molars were made and applied appropriate liners for each groups. After amalgam filling and polishing, polished specimens underwent temperature changed from 5℃ to 55℃ a thousand times. After thermocycling, specimens were placed in 2% methylene blue dye solution for 72 hours in an incubator set at 37℃. The teeth were sectioned buccolingually and the degree of dye penetration was observed with a spectroscopy. (×30) The following results were obtained. 1. Vitrebond, All-bond 2, Superbond D-liner group exhibited a statistically significant lower degree of dye penetration than no liner and copalite group. (Kruskal-Wallis analysis, P<0.05) 2. No liner group and copalite group exhibited a similar degree of dye penetration. (Mann-Whitney analysis, P>0.05) 3. All-bond 2 group exhibited a statistically significant lower degree of dye penetration than Vitrebond group, (Mann-Whitney analysis, P<0.05) Superbond D-liner group also exhibited a lower degree of dye penetration than Vitrebond group but was statistically insignificant. (Mann-Whitney analysis, P>0.05) |
|