| A STUDY ON THE BONDING OF COMPOMER TO DECIDUOUS DENTIN |
| |
| 컴포머와 유치 상아질의 결합에 관한 연구 |
|
김지태, 김용기, 김종수, 권순원 |
|
단국대학교 치과대학 소아치과학 교실 |
|
|
|
|
| Abstract |
|
The purpose of this study was to evaluate the bonding of compomer to deciduous dentin which is known to have been developed to improve the weak properties of glass ionomer cement and composite resin. 120 sound primary molars were used for the shear bond strength test and another 24 for the scanning electron microscopic evaluation. Each material was ailed into polyethylene mold attached to exposed dentinal surface(3×4mm in diameter) of sample blocks. Shearbond strength was measured using Universal testing machine and data were analyzed statistically with Oneway-ANOVA and Scheffe test. Scanning electron microscopic observation was performed in order to evaluate the pattern of distribution and penetration of resin tags and hybrid layer. Compomer groups(II-V) showed significantly higher bond strength values than glass ionomer group(I)(p<.05). Etching-compomer groups(III, V) showed the significantly higher bond strength than non-etching compomer groups(II, IV)(p<.05), but slightly lower values than composite resin group(VI) with no statistically significant difference(p>.05). No significantly different bond strength was found between compomer groups of different bonding system(p>.05). Scanning electron micrographs showed more irregular distribution of short and thin resin tags in non-etching compomer groups(II, IV) whereas the more regular and intimate distribution of long and thick tags in etching compomer groups(III, V) and composite resin group(VI). The evaluation of hybrid layer also showed more regular formation of thicker layer in etching compomer groups(III, V). Based on the results of present study, the use of compomer as an esthetic restorative material for primary molars might be justified. |
| Key Words:
Compomer, Shear bond strength, Resin tag, Dentin bonding agent |
|
PDF Links
Download Citation